1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 | |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Spot analysis | |||||||||||||||
SiO2 | 29.73 | 29.60 | 29.80 | 30.15 | 29.96 | 30.06 | 30.11 | 29.89 | 29.51 | 30.02 | 29.94 | 29.58 | 29.92 | 30.08 | 29.77 |
TiO2 | 38.14 | 37.72 | 36.92 | 36.71 | 37.11 | 36.87 | 37.29 | 36.70 | 37.11 | 37.13 | 36.46 | 37.26 | 36.15 | 37.19 | 37.20 |
Al2O3 | 0.50 | 0.53 | 0.78 | 0.72 | 0.51 | 0.55 | 0.54 | 0.71 | 0.50 | 0.57 | 1.07 | 0.67 | 0.66 | 0.59 | 0.70 |
FeO | 1.22 | 1.36 | 1.44 | 1.51 | 1.25 | 1.04 | 1.18 | 1.33 | 1.20 | 1.11 | 1.45 | 1.13 | 1.60 | 1.20 | 1.38 |
MnO | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 |
MgO | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 |
CaO | 26.88 | 27.55 | 27.83 | 27.46 | 27.76 | 27.89 | 27.25 | 27.63 | 27.52 | 27.14 | 26.93 | 27.23 | 27.31 | 27.85 | 27.50 |
La2O3 | 0.02 | 0.07 | 0.00 | 0.06 | 0.17 | 0.16 | 0.11 | 0.23 | 0.14 | 0.04 | 0.06 | 0.09 | 0.14 | 0.00 | 0.05 |
Nb2O5 | 0.76 | 0.73 | 0.56 | 0.62 | 0.56 | 0.74 | 0.98 | 1.07 | 0.94 | 0.63 | 0.64 | 0.67 | 0.44 | 0.54 | 0.66 |
Total | 97.25 | 97.56 | 97.32 | 97.22 | 97.31 | 97.32 | 97.47 | 97.56 | 97.00 | 96.60 | 96.50 | 96.63 | 96.22 | 97.45 | 97.25 |
On the basis of 5O | |||||||||||||||
Si | 1 | 1 | 1 | 1 | 1.01 | 1.02 | 1.02 | 1.01 | 1 | 1.02 | 1.02 | 1 | 1.02 | 1.01 | 1.01 |
Ti | 0.97 | 0.96 | 0.94 | 0.93 | 0.94 | 0.94 | 0.95 | 0.93 | 0.95 | 0.95 | 0.93 | 0.95 | 0.93 | 0.94 | 0.94 |
Al | 0.01 | 0.02 | 0.03 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.04 | 0.02 | 0.02 | 0.02 | 0.02 |
Fe2 | 0.03 | 0.03 | 0.04 | 0.04 | 0.03 | 0.02 | 0.03 | 0.03 | 0.03 | 0.03 | 0.04 | 0.03 | 0.04 | 0.03 | 0.03 |
Mn | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Mg | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Ca | 0.97 | 1 | 1.01 | 0.99 | 1 | 1.01 | 0.98 | 1 | 1 | 0.98 | 0.98 | 0.99 | 1 | 1 | 0.99 |
Sum | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 | 3.00 |