From: Fabrication of dense albite aggregates by hot pressing
Exp. No. | Archimedes' method | Shape measurement | ||||||
---|---|---|---|---|---|---|---|---|
Weight (g) | Buoyancy force (gw) | Standard deviation (gw) | Volume (cm3) | Apparent density (× 103 kg m−3) | Apparent porosity (%) | Apparent density (× 103 kg m−3) | Apparent porosity (%) | |
#1 | 6.52 | 2.60 | 0.01 | 2.61 | 2.50 | 4.52 | 2.58 | 1.50 |
#2 | 7.10 | 2.86 | 0.01 | 2.87 | 2.48 | 5.53 | 2.55 | 2.73 |
#3 | 7.10 | 3.80 | 0.01 | 3.81 | 1.87 | 28.81 | 1.79 | 31.62 |
#4 | – | – | – | – | – | – | 1.48 | 43.64 |
#5 | – | – | – | – | – | – | 1.67 | 36.33 |
#6 | 6.77 | 3.08 | 0.01 | 3.09 | 2.19 | 16.26 | 2.13 | 18.66 |
#7 | 6.79 | 2.66 | 0.00 | 2.67 | 2.54 | 2.87 | 2.48 | 5.20 |
#8 | 23.71 | 9.10 | 0.01 | 9.12 | 2.60 | 0.74 | 2.62 | 0.15 |
#9 | 17.92 | 8.16 | 0.03 | 8.18 | 2.19 | 16.37 | 2.22 | 15.18 |
#10 | 20.68 | 8.25 | 0.02 | 8.27 | 2.50 | 4.54 | 2.54 | 3.24 |
#11 | 18.12 | 7.26 | 0.01 | 7.27 | 2.49 | 4.84 | 2.31 | 11.89 |
#12 | 15.12 | 5.93 | 0.01 | 5.94 | 2.55 | 2.83 | 2.50 | 4.74 |
#13 | 2.43 | 0.93 | 0.01 | 0.93 | 2.61 | 0.27 | 2.62 | 0.10 |
#14 | 19.51 | 8.16 | 0.01 | 8.17 | 2.39 | 8.87 | 2.37 | 9.53 |
#15 | 11.12 | 4.42 | 0.03 | 4.43 | 2.51 | 4.22 | 2.51 | 4.38 |
#16 | 14.78 | 5.64 | 0.01 | 5.65 | 2.62 | 0.16 | 2.62 | 0.13 |
#17 | 14.27 | 5.45 | 0.02 | 5.46 | 2.61 | 0.32 | 2.62 | 0.07 |
#18 | 1.04 | 0.40 | 0.01 | 0.40 | 2.61 | 0.53 | 2.62 | 0.04 |