From: Fabrication of dense albite aggregates by hot pressing
Exp. No. | Weight (g) | Shape | Bottom area (mm2) | Height (mm) | Volume (cm3) | Apparent density (× 103 kg m−3) | Apparent porosity (%) | Visual appearance | Partial melt? |
---|---|---|---|---|---|---|---|---|---|
#1 | 6.97 | Cylinder | 186.27 | 14.50 | 2.70 | 2.58 | 1.5 | Black | P. melt |
#2 | 7.55 | Cylinder | 188.69 | 15.70 | 2.96 | 2.55 | 2.7 | Black and white mottled | P. melt |
#3 | 7.90 | Cylinder | 205.10 | 21.50 | 4.41 | 1.79 | 31.6 | White | – |
#4 | 7.74 | Cylinder | 202.07 | 25.94 | 5.24 | 1.48 | 43.6 | White | – |
#5 | 59.27 | Rectangular | 1974.00 | 18.00 | 35.53 | 1.67 | 36.3 | White | – |
#6 | 7.02 | Cylinder | 204.85 | 16.08 | 3.29 | 2.13 | 18.7 | Grey and white mottled | P. melt |
#7 | 7.13 | Cylinder | 203.58 | 14.10 | 2.87 | 2.48 | 5.2 | Black and white mottled | P. melt |
#8 | 32.018 | Rectangular | 1974.00 | 6.20 | 12.24 | 2.62 | 0.1 | Black (white mottled) | P. melt |
#9 | 18.50 | Cylinder | 339.79 | 24.50 | 8.32 | 2.22 | 15.2 | Grey and white mottled | – |
#10 | 20.675 | Cylinder | 339.79 | 24.00 | 8.16 | 2.54 | 3.2 | Black and white mottled | – |
#11 | 17.89 | Cylinder | 356.33 | 21.75 | 7.75 | 2.31 | 11.9 | Black (partly white) | – |
#12 | 16.60 | Cylinder | 346.36 | 19.20 | 6.65 | 2.50 | 4.7 | Black (partly white) | – |
#13 | 23.56 | Cylinder | 350.66 | 25.67 | 9.00 | 2.62 | 0.1 | White | – |
#14 | 19.79 | Rectangular | 780.30 | 10.70 | 8.35 | 2.37 | 9.5 | White | – |
#15 | 22.55 | Rectangular | 779.28 | 11.55 | 9.00 | 2.51 | 4.4 | White | – |
#16 | 29.80 | Rectangular | 785.40 | 14.50 | 11.39 | 2.62 | 0.1 | Black | – |
#17 | 27.76 | Rectangular | 785.40 | 13.50 | 10.60 | 2.62 | 0.1 | Greenish grey | – |
#18 | 30.01 | Rectangular | 785.40 | 14.59 | 11.46 | 2.62 | 0.04 | White | – |