Fig. 6 | Progress in Earth and Planetary Science

Fig. 6

From: Fabrication of dense albite aggregates by hot pressing

Fig. 6

SEM images of hot-pressed samples prepared from the powders after 6 h of decantation. a Backscattered electron image (BEI) of the sample that was hot-pressed at 50 MPa and 1150 °C (Exp. #1). b BEI of the sample that was hot-pressed at 50 MPa and 1125 °C (Exp. #2). c Secondary electron image (SEI) of the sample that was hot-pressed at 50 MPa and 1050 °C (Exp. #5)