Table 2 Pressure dependences of d-spacings (Ã…) and a6D (Ã…) from the characteristic peaks

From: Can quasicrystals survive in planetary collisions?

PNe (GPa)

V (Ã…3)

a6d

(8,4)

(12,16)

(24,36)

(28,44)

(32,48)

(44,64)

(56,84)

(60,92)

(72,116)

(80,128)

0.0

2020.96

12.6431

8.94

5.53

3.750

3.410

3.240

2.799

2.451

2.350

2.108

2.006

5.0

1938.85

12.4695

8.82

5.44

3.698

3.368

3.201

2.760

2.420

2.319

2.080

1.979

5.6

1929.35

12.4491

8.80

5.45

3.696

3.366

3.203

2.759

2.420

2.319

2.081

1.979

21.8

1746.67

12.0431

8.52

5.26

3.566

3.252

3.092

2.669

2.339

2.239

2.009

1.912

22.7

1747.89

12.0459

8.52

5.27

3.571

3.251

3.094

2.665

2.338

2.241

2.012

1.912

35.4

1637.86

11.7876

8.33

5.16

3.495

3.181

3.021

2.609

2.326

2.194

1.971

1.872

37.0

1611.29

11.7235

8.29

5.14

3.478

3.164

3.007

2.593

2.320

2.185

1.952

1.862

42.8

1617.61

11.7388

8.30

5.13

3.479

3.161

3.009

2.593

2.321

2.180

1.954

1.858

40.0

1608.28

11.7162

8.28

5.13

3.476

3.163

3.007

2.594

2.320

2.183

1.953

1.858

40.0

1606.81

11.7126

8.28

5.14

3.477

3.168

3.007

2.593

2.320

2.183

1.954

1.862

51.0

1571.31

11.6257

8.22

5.07

3.447

3.133

2.986

2.573

2.305

2.158

1.941

1.846

53.8

1562.72

11.6045

8.21

5.05

3.437

3.127

2.977

2.562

2.303

2.153

1.935

1.840

56.8

1556.76

11.5897

8.19

5.04

3.427

3.118

2.968

2.558

2.296

2.147

1.930

1.835

60.5

1528.91

11.5202

8.15

5.04

3.414

3.113

2.956

2.550

2.287

2.140

1.921

1.829

63.5

1520.63

11.4994

8.13

5.02

3.406

3.106

2.949

2.541

2.278

2.137

1.916

1.824

66.5

1507.03

11.4650

8.11

5.01

3.397

3.098

2.940

2.533

2.280

2.129

1.911

1.819

68.0

1501.09

11.4499

8.10

4.99

3.396

3.093

2.936

2.533

2.281

2.128

1.908

1.816

71.0

1484.92

11.4087

8.07

4.98

3.386

3.085

2.926

2.526

2.277

2.119

1.901

1.811

71.5

1481.15

11.3990

8.06

4.97

3.391

3.095

2.935

–

2.281

2.120

1.906

1.815

75.8

1453.00

11.3263

8.01

4.95

3.380

3.075

2.925

–

2.277

2.116

1.897

1.812

74.5

1452.88

11.3260

8.01

4.96

3.375

3.076

2.920

2.515

2.271

2.115

1.897

1.806

74.5

1449.65

11.3176

8.00

4.97

3.375

3.073

2.916

2.516

2.278

2.119

1.902

1.805

54.0

1570.54

11.6238

8.22

5.08

3.453

3.141

2.986

2.575

–

–

1.944

1.846

27.8

1712.36

11.9637

8.46

–

3.565

3.237

3.077

–

–

–

–

–