From: Melting phase relations in the MgSiO3–CaSiO3 system at 24 GPa
Bdg | CaPv | Pc | |
---|---|---|---|
T 0 (K) | 300 | 300 | 300 |
V 0 (cm3/mol) | 24.45 | 27.45 | 11.24 |
K T0 (GPa) | 251(3) | 236(4) | 161(3) |
K T0′ | 4.1(1) | 3.9(2) | 3.8(2) |
γ 0 | 1.57(5) | 1.89(7) | 1.36(5) |
q 0 | 1.1(3) | 0.9(16) | 1.7(2) |
θ 0 (K) | 905(5) | 796(44) | 767(9) |
F 0 (kJ/mol) | − 1368(1) | − 1463(8) | − 569 |